3V forging machetes.
This is my recently produced machetes forging 3V.
Is the first time I use the "3V" This steel.
Forging steel hardware than feeling soft than D2.
Forging will be burnt if the first break.
But still manage to forge.
After forging a natural feeling, such as hardening 01.
Annealing to return to many times.
After forging, such as grinding feeling S30V
Super durable.
But really, if enough material.
I think that with the exception of grinding would be more appropriate.
Introduced it to come back this knife.
3V steel forging.
303 stainless steel hand.
Is used with the aluminum pads and gaskets.
Fossil ivory handle is wood. Nail mosaic. Stainless steel tube.
Sheath material is leather.
Picture it.
3V鍛造砍刀.
這是我最近製作的3V鍛造砍刀.
也是我第一次使用"3V"這種鋼材.
鍛造的感覺比碳鋼硬比D2軟．
如果燒過頭鍛造會碎裂．
但是還是勉強可以鍛造．
鍛造後的感覺如０１自然硬化．
要多次退火才能回復．
鍛造後研磨的感覺如S30V
超級耐磨的．
不過說真的如果材料夠．
我覺得還是用磨除會更適當．
回來介紹這支刀子吧．
鋼材3V鍛造．
３０３不銹鋼護手．
用的是黑墊片與鋁墊片．
柄材是象牙化石．馬賽克釘．不銹鋼管．
鞘材是牛皮．
看圖吧．
This is my recently produced machetes forging 3V.
Is the first time I use the "3V" This steel.
Forging steel hardware than feeling soft than D2.
Forging will be burnt if the first break.
But still manage to forge.
After forging a natural feeling, such as hardening 01.
Annealing to return to many times.
After forging, such as grinding feeling S30V
Super durable.
But really, if enough material.
I think that with the exception of grinding would be more appropriate.
Introduced it to come back this knife.
3V steel forging.
303 stainless steel hand.
Is used with the aluminum pads and gaskets.
Fossil ivory handle is wood. Nail mosaic. Stainless steel tube.
Sheath material is leather.
Picture it.
3V鍛造砍刀.
這是我最近製作的3V鍛造砍刀.
也是我第一次使用"3V"這種鋼材.
鍛造的感覺比碳鋼硬比D2軟．
如果燒過頭鍛造會碎裂．
但是還是勉強可以鍛造．
鍛造後的感覺如０１自然硬化．
要多次退火才能回復．
鍛造後研磨的感覺如S30V
超級耐磨的．
不過說真的如果材料夠．
我覺得還是用磨除會更適當．
回來介紹這支刀子吧．
鋼材3V鍛造．
３０３不銹鋼護手．
用的是黑墊片與鋁墊片．
柄材是象牙化石．馬賽克釘．不銹鋼管．
鞘材是牛皮．
看圖吧．
What you have seen.