Here is one I finished today!!
It is what I would call a utility, what would you call it?
Its made from 1/8 1084 that I heat treated myself
I am keeping this one for testing purposes.
OAL - 8 9/16
Edge - 3 13/16
Handle - 4 5/16
Hand rubbed to 400 grit
Scales are Spalted Birch that I stabilized myself.
Nickel/Silver Pins
It is what I would call a utility, what would you call it?
Its made from 1/8 1084 that I heat treated myself
I am keeping this one for testing purposes.
OAL - 8 9/16
Edge - 3 13/16
Handle - 4 5/16
Hand rubbed to 400 grit
Scales are Spalted Birch that I stabilized myself.
Nickel/Silver Pins