Does anyone know what angle Buck sharpens to?

Thank you everyone. I thinned out my sharpening edge and now my 501 is as sharp as I would expect.

I have a pair of Spyderco ceramic benchstones that I may try using to make a micro bevel.

Thank you everyone.
 
Ok, thank you. But SiC is harder than aluminum oxide ceramic. If your wanting to shape the vanadium carbides. Then diamond or boride is what will cut it. DM
 