Will it cause some bad thing like fire or anything? I want to anodize a glassbreaker, which is Tungsten carbide tip attached to titanium. I have anodized framelock by using Al foil added into hydrogen peroxide before.
 
Add nail polish to the tungsten portion. It wont react with the anodizing solution if covered.

If not covered it may react negatively. But I am not sure, never had anything that had tungsten in it. I always cover any non titanium surface with nail polish to prevent unwanted reactions.
 