heat treating

Couldn't find HT info on internet but it doesn't have very much in it .If it's from a saw blade , normalize from 1500 F, then harden from 1500 F ,quench in fast oil. Temper 400 F. 74NiCr2 - C .74, Si .17, Mn .40, Cr .25, Ni .55
 